MOCVD precursors based on organometalloid ligands

ABSTRACT

Chemical vapor deposition processes utilize as precursors volatile metal complexes with ligands containing metalloid elements silicon, germanium, tin or lead.

RELATED APPLICATIONS

This application is a continuation-in-part of Ser. No. 09/314,311, filed on May 19, 1999, now U.S. Pat. No.6,184,409 B1 the contents of which incorporated herein by reference.

FIELD OF INVENTION

This invention relates to organometalloid compounds and metal complexes thereof, which are of use for chemical vapor deposition processes and in other chemical processes.

BACKGROUND OF THE INVENTION

As the microelectronics industry moves into ultralarge scale integration (ULSI), enhancement in performance speeds of integrated circuits will be achieved by reducing the device feature size and thereby the overall die size. As a result, density constraints will require multilevel structures with vertical interconnects. It is expected that the use of metals with lower resistivity, such as gold, silver and especially copper, will be necessary because of the submicron geometries.

Fabrication of interconnect structures includes one or more metallization steps. Metallization is commonly accomplished by physical vapor deposition (PVD) processes, including evaporating and sputtering. Chemical vapor deposition (CVD) processes have an advantage over these so-called “line of sight” processes in the fabrication of submicron vertical interconnects because conformal layers of metals are more easily produced.

In CVD, a volatile precursor, usually a complex of a metal with an organic ligand, serves as a source of the metal. The precursor is delivered to the substrate in the vapor phase and decomposed on the surface to release the metal. The precursor must exhibit sufficient thermal stability to prevent premature degradation or contamination of the substrate and at the same time facilitate easy handling. Vapor pressure, the adsorption/desorption behaviour, the chemical reaction pathways, and the decomposition temperature can directly affect the purity of the deposited metal film and the rate of thin-film formation.

CVD precursors very frequently are based on complexes of metals with β-diketonates such as 2,2,6,6-tetramethyl-3,5-heptanedione (thd) and acetylacetonate (acac) and fluorinated b-diketonates, such as 1,1,1,5,5,5-hexafluoro-2,4-pentanedione (hfa or hfac) and 2,2-diethyl-6,6,7,7,8,8,8-heptafluoro-3,5-octanedione (fod). Volatility of the non-fluorinated precursors is insufficient for many applications. The fluorinated analogs possess greater volatility, but also have a tendency to fragment, a consequence of fluorine migration/carbon-fluorine bond cleavage at elevated temperatures, leading to contamination of the substrate. Consequently, a need exists for precursors which retain volatility yet release the metal without degradation of the ligand and for ligands which are not labile or disposed toward fragmentation.

It is therefore an object of this invention to develop metal complexes for CVD precursors that are highly volatile and yet stable at the sublimation point and also retain desirable processing features. It is a further object to develop ligands for use in CVD precursors which can induce high volatility in a metal and can release the metal without degradation of the ligand. It is a further object to provide new synthetic routes for the synthesis of these ligands from commercially available starting materials in good yields.

SUMMARY OF THE INVENTION

It has been surprisingly discovered that certain organic compounds containing silicon, germanium, tin or lead, when complexed with a metal, can induce high volatility in the metal complex. The resulting complexes are stable at the sublimation point and retain desirable processing features. The compounds have the structure of formula I:

wherein

R¹ is C₂ or higher alkyl, substituted alkyl, haloalkyl, cycloalkyl, C₇ or higher aryl, substituted aryl, heteroaryl, arylalkyl, alkoxy, acyl, alkyl carboxylate, aryl carboxylate, alkenyl, alkynyl, or E²(R⁶)(R⁷)(R⁸);

R² is H, halogen, nitro, or haloalkyl;

E¹ and E² are independently Si, Ge, Sn, or Pb;

R³, R⁴, R⁵, R⁶, R⁷, and R⁸ are independently chosen from alkyl, substituted alkyl, cycloalkyl, aryl, substituted aryl, arylalkyl, alkoxy, alkenyl, alkynyl or R⁴ and R^(5,) or R⁷ and R⁸ taken together form a divalent alkyl radical;

Y and Z are independently O, S or NR⁹; and

R⁹ is alkyl, substituted alkyl, cycloalkyl, aryl, substituted aryl, heteroaryl, arylalkyl, alkoxy, alkenyl, or alkynyl.

The present invention also relates to metal-ligand complexes that are highly volatile and yet stable at the sublimation point. The complexes also retain desirable processing features. The metal complexes of the present invention have the structure of formula II:

M L_(n)·pD  (II)

wherein

M is a metal chosen from the group consisting of: Li, Na, K, Rb, Cs, Mg, Ca, Sr, Ba, Sc, Y, La, Ce, Ti, Zr, Hf, Pr, V, Nb, Ta, Nd, Cr, Mo, W, Mn, Re, Sm, Fe, Ru, Eu, Os, Co, Rh, Ir, Gd, Ni, Pd, Pt, Tb, Cu, Ag, Au, Dy, Ho, Al, Ga, In, Tl, Er, Ge, Sn, Pb, Tm, Sb, Bi, Yb, Lu, Th, and U;

D is a neutral coordinating ligand;

n is equal to the valence of M;

p is zero or an integer from 1 to 6; and

L is a compound of formula III:

 wherein

R¹ is alkyl, substituted alkyl, haloalkyl, cycloalkyl, aryl, substituted aryl, heteroaryl, arylalkyl, alkoxy, acyl, alkyl carboxylate, aryl carboxylate, alkenyl, alkynyl, or E²(R⁶)(R⁷)(R⁸);

R²is H, halogen, nitro, or haloalkyl;

E¹ and E² are independently Si, Ge, Sn, or Pb;

R³ , R⁴, R⁵, R⁶, R⁷, and R⁸ are independently chosen from alkyl, substituted alkyl, cycloalkyl, aryl, substituted aryl, arylalkyl, alkoxy, alkenyl, alkynyl or R⁴ and R⁵, or R⁷ and R⁸ taken together form a divalent alkyl radical;

Y and Z are independently O, S or NR⁹; and

R⁹ is alkyl, substituted alkyl, cycloalkyl, aryl, substituted aryl, heteroaryl, arylalkyl, alkoxy, alkenyl, or alkynyl.

In another aspect, the present invention relates to a method of depositing a metal-containing layer on a substrate comprising vaporizing a metal-ligand complex of formula II and decomposing the metal-ligand complex in the presence of the substrate.

In yet another aspect, the present invention relates to ligands having haloalkyl-substituted metalloid substituents, particularly fluoroalkyl-substituted. In this case, R³, R⁴, R⁵,R⁶,R⁷, and R⁸ are independently alkyl or haloalkyl, and at least one of R³,R⁴,R⁵,R⁶, R⁷, and R⁸ is haloalkyl.

New synthetic routes for the synthesis of the ligands of formula I from commercially available starting materials in good yields have been discovered. In yet another aspect, the present invention relates to processes for preparing the ligands of formula I and metal complexes of formula II.

DETAILED DESCRIPTION OF THE INVENTION

The present invention relates to organometalloid compounds that confer volatility on a metal when complexed therewith. Metalloids are defined herein as the elements silicon, germanium, tin and lead. Organometalloids are defined as compounds containing one or more metalloid atoms bonded to a carbon atom. The organometalloid compounds of the present invention have the structure of formula I:

wherein

R¹ is C₂ or higher alkyl, substituted alkyl, haloalkyl, haloalkyl, cycloalkyl, C₇ or higher aryl, substituted aryl, heteroaryl, arylalkyl, alkoxy, acyl, alkyl carboxylate, aryl carboxylate, alkenyl, alkynyl, or E²(R⁶)(R⁷)(R⁸);

R² is H, halogen, nitro, or haloalkyl;

E¹ and E² are independently Si, Ge, Sn, or Pb;

R³, R⁴, R⁵, R⁶, R⁷, and R⁸ are independently chosen from alkyl, substituted alkyl, cycloalkyl, aryl, substituted aryl, arylalkyl, alkoxy, alkenyl, alkynyl or R⁴ and R⁵, or R⁷ and R⁸ taken together form a divalent alkyl radical;

Y and Z are independently O, S or NR⁹; and

R⁹ is alkyl, substituted alkyl, cycloalkyl, aryl, substituted aryl, heteroaryl, arylalkyl, alkoxy, alkenyl, or alkynyl.

In a preferred embodiment, I is a silyl β-diketonate or a silyl β-thioketonate and R¹ is C₂ or higher alkyl, C₇ or higher aryl, or haloalkyl; R² is H; R³, R⁴, and R⁵ are methyl; E¹ is Si; and Y and Z are independently O or S.

In a more preferred embodiment, R¹ is ethyl, isopropyl, n-propyl, isobutyl, n-butyl, t-butyl, trifluoromethyl, heptafluoropropyl, 2-propenyl or phenyl; E¹ is Si; and Y and Z are O or Y is S and Z is O.

In an even more preferred embodiment the compound is one of those appearing in Table 1:

TABLE 1

In another embodiment, R¹ is methyl, ethyl, isopropyl, n-propyl, isobutyl, s-butyl, n-butyl, CF₃,C₂F₅, i-C₃F₇, n-C₃F₇, or —C(CH₃)(CF₃)₂; R² is H; E¹ is Si or Ge; R³, R⁴, and R⁵ are independently C₆ or lower alkyl; and Y and Z are O. α-Germa-β-diketones (formula I, where E¹ is Ge) are of particular interest.

In yet another embodiment, R³, R⁴, and R⁵ are independently haloalkyl or alkyl. In this embodiment, R³, R⁴, R⁵, R⁶, R⁷, and R⁸ are independently alkyl or haloalkyl, and at least one of R³, R⁴, R⁵, R⁶, R⁷, and R⁸ is haloalkyl. In particular, E¹ is Si, or at least one of R³, R⁴, R⁵, R⁶, R⁷, and R⁸ are independently fluoroalkyl, specifically C₃ or higher fluoroalkyl. The organometalloid compound may be an α-sila, β-diketonate wherein R¹ is alkyl, or haloalkyl; R² is H; E¹ is Si; X and Y are O; and R³, R⁴, and R⁵ are independently alkyl or haloalkyl, and at least one of R³, R⁴, R⁵, R⁶, R⁷, and R⁸ is haloalkyl. In particular, R¹ may be alkyl or haloalkyl, R³ and R⁴ methyl, and R⁵ is (CH₂)₂(CF₂)₅CF₃ or (CH₂)₂(CF₂)₇CF₃; in specific embodiments, R¹ is methyl, n-propyl, t-butyl, CF₃,C₂F₅, or n-C₃F₇.

The volatile metal complexes of the present invention are useful in processes which deposit a metal on a substrate from a vapor phase, such as metal organic chemical vapor deposition (MOCVD), molecular beam epitaxy (MBE) and atomic layer epitaxy (ALE). They have the structure of formula II:

M L_(n)·pD  (II)

wherein

M is a metal chosen from the group consisting of: Li, Na, K, Rb, Cs, Mg, Ca, Sr, Ba, Sc, Y, La, Ce, Ti, Zr, Hf, Pr, V, Nb, Ta, Nd, Cr, Mo, W, Mn, Re, Sm, Fe, Ru, Eu, Os, Co, Rh, Ir, Gd, Ni, Pd, Pt, Tb, Cu, Ag, Au, Dy, Ho, Al, Ga, In, Tl, Er, Ge, Sn, Pb, Tm, Sb, Bi, Yb, Lu, Th, and U;

D is a neutral coordinating ligand;

n is equal to the valence of M;

p is zero or an integer from 1 to 6; and

L is a ligand of formula III:

 wherein

R¹ is alkyl, substituted alkyl, haloalkyl, cycloalkyl, aryl, substituted aryl, heteroaryl, arylalkyl, alkoxy, acyl, alkyl carboxylate, aryl carboxylate, alkenyl, alkynyl, or E²(R⁶)(R⁷)(R⁸);

R² is H, halogen, nitro, or haloalkyl;

E¹ and E² are independently Si, Ge, Sn, or Pb;

R³, R⁴, R⁵, R⁶, R⁷, and R⁸ are independently chosen from alkyl, substituted alkyl, cycloalkyl, aryl, substituted aryl, arylalkyl, alkoxy, alkenyl, alkynyl or R⁴ and R⁵, or R⁷ and R⁸ taken together form a divalent alkyl radical;

Y and Z are independently O, S or NR⁹; and

R⁹ is alkyl, substituted alkyl, cycloalkyl, aryl, substituted aryl, heteroaryl, arylalkyl, alkoxy, alkenyl, or alkynyl.

Preferred metals are Cu, Co, Mn, Ag, In, Ce, Sr, Ba, Ru, or Au. More preferred metals are Cu and Ag. In some embodiments, Pd and Pt are preferred metals. Preferred ligands are the preferred organometalloid compounds described above. In particular, ligands of formula III, wherein R¹ is methyl, ethyl, isopropyl, n-propyl, isobutyl, s-butyl, n-butyl, CF₃, C₂F₅, i-C₃F₇, n-C₃F₇, or —C(CH₃)(CF₃)₂; R² is H; E¹ is Si or Ge; R³, R⁴, and R⁵ are independently C₆ or lower alkyl; and Y and Z are O, may be used. α-Germa-β-diketones (formula III, where E¹ is Ge) may also be used.

Ligands having reduced oxygen content can reduce oxygen contamination of the substrate during metal deposition. Preferred metal complexes are listed in Table 2:

TABLE 2 CU((CH₃)₃CCOCHCOSi(CH₃)₃)₂ CU(CF₃COCHCOSi(CH₃)₃)₂ CU((CH₃COCHCOSi(CH₃)₃)₂ CU((CH₃)₂CHCH₂COCHCOSi(CH₃)₃)₂ CU(CH₃CH₂COCHCOSi(CH₃)₃)₂ CU(CF₃(CF₂)₂COCHCOSi(CH₃)₃)₂ CU(CH₃CH₂CH₂COCHCOSi(CH₃)₃)₂ CU(C₆H₅COCHCOSi(CH₃)₃)₂ CU(CH₃(CH₂)₃COCHCOSi(CH₃)₃)₂ CU(H₂C═(CH₃)CCCHCOSi(CH₃)₃)₂ CU((CH₃)₂CHCOCHCOSi(CH₃)₃)₂ Co((CH₃)₃CCOCHCOSi(CH₃)₃)₃ Ag((CH₃)₃CCOCHCOSi(CH₃)₃) Mn((CH₃)₃CCOCHCOSi(CH₃)₃)₃

The term “complex” is intended to be broadly construed to encompass compounds as well as coordination complexes wherein at least one metal atom is covalently, ionically or associatively coordinated to at least one organic ligand group. Accordingly, the metal complexes of the present invention may contain one or more neutral coordinating ligands (D in formula II) in addition to the organometalloid ligands described above, in particular when the metal has a valence of one. Suitable coordinating ligands include Lewis bases such as vinyltrimethylsilane (VTMS), bis-(trimethylsilyl) acetylene, 1,5-cyclooctadiene (COD), 1,6-dimethyl-1,5-cyclooctadiene, alkyl phosphines, alkynes, such as trimethylsilylalkyne (TMSA) and mixtures thereof.

In another embodiment, the present invention relates to metal complexes with fluorinated ligands, that is, where R³, R⁴, R⁵, R⁶, R⁷, and R⁸ are independently chosen from alkyl and haloalkyl, and at least one of R³, R⁴, R⁵, R⁶, R⁷, and R⁸ is haloalkyl. These complexes exhibit unexpected order in the solid state, in particular where E¹ is Si and at least one of R³, R⁴, or R⁵ is C₃ or higher fluoroalkyl. This is illustrated by the crystal structure of a complex where M is copper, R³ and R⁴ are methyl and R⁵ is (CH₂)₂(CF₂)₇CF₃, as determined by x-ray diffraction. The structure is shown in FIG. 1. It can be seen from the figure that the perfluoroalkyl groups of one molecule associate with the perfluoroalkyl groups of other molecules in an orderly, interdigitated manner. The result is formation of a distinct fluorous region in the crystal.

Nanostructured materials composed of these complexes may contain separate fluorine- and /or metal-containing regions, domains, areas or layers, depending on the composition of the complex(es) employed, and method of fabricating the nanostructured materials. These regions may have oxophilic, fluorophilic, lipophilic and/or hydrophilic properties, and are, therefore, are useful in many applications. Fluoroalkyl domains are typically optically transparent and possess low k properties. Nanostructured materials having such domains may be used as nanoscale slits for microelectrooptical devices or as micromagnetic domains for data storage. Where self-organized Langmuir Blodget films are formed, the nanostructured materials may be used as magnetically sensitive thin films. In addition, the materials may be useful as organized catalysts. For example, a fluorocarbon interlayer may facilitate selective accumulation of reactants in oxidative transformations where the oxidized product might be protected from overoxidation due to limited solubility of the more polar product in the fluorous or fluorophilic phase. In particular, where the nanostructured material consists of a bimetallic catalyst created by combination of a mixture of two or more complexes, such as a mixture of a copper complex with a palladium complex, thin film catalysts for oxidative transformations may be formed.

Synthetic methods for the preparation of β-diketones are numerous and well documented. However, application of these strategies to the synthesis of silyl β-diketonates is frequently unsuccessful, due to the reactivity of the product to the reagents or reaction conditions, and to the occurrence of side reactions via the cleavage of the carbonyl-silicon bond. Therefore, it is preferred that the organometalloid compounds of the present invention be prepared by the processes of the present invention.

The organometalloid compounds may be prepared by a Claisen condensation between a lithium enolate anion and an acyl, thioacyl or imino compound having a leaving group adjacent to the unsaturated group. This reaction is illustrated in Scheme 1:

In Scheme 1, R¹, R², R³, R⁴, R⁵, R⁶, R⁷, R⁸, R⁹, E¹, Y and Z are as defined for the compounds of formula I, above, R is alkyl, and Q is a leaving group. Suitable leaving groups for the process are halo, acyl, alkoxy, phenoxy, amido, dialkylamino, and alkoxyamino. Preferably, R¹C(Y)Q is an acid chloride or an ester. In the synthesis of non-fluorinated silyl-β-diketones, R¹C(Y)Q is preferably an acid chloride. The procedure may also be used for the synthesis of fluorinated derivatives, that is, where one or more of R¹, R³, R⁴, or R⁵ are fluoroalkyl groups. Yields are typically lower than with non-fluorinated derivatives, presumably because of the enhanced acidity of the fluorinated β-diketonates and the pursuant rapid protonation of the enolate. Therefore, it may be desirable to employ a variation of the process of Scheme 1, illustrated in Scheme 1a, for the preparation of fluorinated β-diketones. In this procedure, base is added to a mixture of the two starting materials. Either lithium diamine (LDA) or NaH may be utilized as bases. Even in the presence of good electrophiles, the desired β-diketones may be formed. When the perfluoroacid ester or acid fluorides were employed instead of acid chlorides at elevated temperature (−20° to −40° C.), higher yields of the fluorinated β-diketones, with almost complete consumption of the starting acylsilanes, resulted.

In another embodiment, the organometalloid compounds are prepared as illustrated in Scheme 2. A thioketal-protected acylmetalloid is reacted with an alkyllithium compound, such as n-butyl lithium, and the product is subsequently reacted with a copper salt to form a protected lithium dithianylmetalloid cuprate. The cuprate is then reacted with an appropriate α-bromoketone or α-bromo-thioketone. The thioketal protecting group can be removed by methods described in the literature. Preferably the deprotection is accomplished by treatment with a suitable mercury reagent. An example of an effective mercury reagent is a combination of mercuric oxide and mercuric chloride.

The metal complexes of the present invention may be prepared by reacting the organometalloid compounds synthesized as described above with a metal salt under protic or aprotic conditions. The ligand is dissolved in a suitable solvent and the anion of the ligand is formed by abstraction of a proton with base. The metal salt is then added, and the resulting metal ligand complex is isolated by removal of the solvent and crystallized. Under protic conditions, a protic base such as sodium hydroxide, may be used, with a protic solvent, such as an aqueous alcohol. Similarly under aprotic conditions, aprotic bases and solvents may be used. An example of a suitable aprotic solvent is tetrahydrofuran; an example of a suitable aprotic base is potassium hydride.

In another embodiment, the metal complexes may be prepared directly as shown in Scheme 3.

In Scheme 3, R¹, R², R³, R⁴, R⁵, R⁶, R⁷, R⁸, R^(9, E) ¹, Y and Z are as defined for the compounds of formula III, above, and R is alkyl or phenyl. The starting lithium metalloid compound of formula E¹R³R⁴R⁵Li is prepared according to the method described in the literature(Still, W. C., J. Org. Chem., 41, 3063-3064 (1976)). The lithiummetalloid compound is then reacted with an appropriate compound, as depicted in Scheme 3, for example, a β-diketone, a β-thioketone, or a β-ketoimine, to yield a ligand of formula III. Without isolating the product, a metal salt is added to form a complex of the metal with the ligand.

Acylgermane compounds for use in synthesis of α-germa-β-diketones may be prepared via the metallation of ethyl vinyl ether. Scheme 4 illustrates a process in which acetyl trimethylgermane is prepared from ethyl vinyl ether and chlorotrimethyl-germane. Chlorotrimethylgermane, alternately listed as trimethylgermanium chloride, is commercially available, for example, from Aldrich. α-Germa-β-diketones may be synthesized by the procedures described for the synthesis of the α-sila-β-diketones, including those illustrated in Schemes 1 and 1a, and particularly by that in Scheme 1. Similarly, metal complexes with α-germa-β-diketones may be prepared by the methods shown in Schemes 2 and 3.

Processes whereby metals are deposited from volatile precursors are utilized in many different microelectronics applications. Metals such as Li, Na, K, Rb, Cs, Mg, Ca, Sr, Ba, Sc, Y, La, or Ce are typically used in applications such as high k dielectrics, superconductors, and high refractive index materials, although their use is not limited to these applications. Metals such as Ti, Zr, Hf, Pr, V, Nb, Ta, Nd, Cr, Mo, W, Mn, Re, or Sm are typically used in microelectronic applications chemically combined with nitrogen or silicon as the nitride or silicide for use as barrier materials or hard coatings, although, again, their use is not limited to these applications. Metals such as Fe, Ru, Eu, Os, Co, Rh, Ir, Gd, Ni, Pd, Pt, Tb, Cu, Ag, Au, Dy, Zn, Cd, Hg, Ho, Al, Ga, In, Tl, and Er are typically used in electronics applications as metals, or metal alloys, in particular, as metal or metal alloy films for interconnects, electrodes, and mirrors, although, again, their use is not limited to these applications. Metals and metalloids such as Si, Ge, Sn, Pb, Tm, Sb, Bi, Yb, and Lu are typically used in microelectronic devices and as semiconductors, although, again, their use is not limited to these applications.

The metal complexes of the present invention may be deposited on a substrate to form a layer of one or more metals in the form of the metal or of particular inorganic compounds, for example as an oxide, a hydroxide, a carbonate, a silicide or a nitride. It will be apparent to a person skilled in the art that, if desired, he may use not only a particular compound of formula II but also mixtures of such compounds in which M, L, or both vary. A metal complex is advantageously decomposed in the vapor phase by a metal organic chemical vapor deposition (MOCVD), molecular beam epitaxy (MBE) or atomic layer epitaxy (ALE) process. The principle of these processes and suitable apparatuses for these purposes are well known in the art.

Typically, an apparatus for deposition from the vapor phase is pressure tight and can be evacuated. The substrate which is to be coated is to be introduced into this apparatus. Under reduced pressure the complex of formula II is vaporized. If desired, inert or reactive gas may be present in the apparatus in addition to the complex of the present invention in the vapor state.

The metal complex, in vapor form, is typically continuously or intermittently introduced into the apparatus via a special line. In some cases the metal complex may be introduced into the apparatus together with the substrate which is to be coated and not vaporized until it is within the apparatus. A carrier gas may optionally be used to aid in transporting the metal complex into the apparatus. The vaporization of the metal complex can be promoted by heating and if desired by the addition of the carrier gas.

Decomposition of the substrate may be effected by known methods. In general, these are thermal decomposition, plasma-or radiation-induced decomposition and/or photolytic decomposition. Thermal decomposition from the vapor phase is usually performed so that the walls of the apparatus are kept cold and the substrate is heated to a temperature at which the desired layer is deposited on the substrate. The minimum temperature required for decomposition of the compound may be determined in each case by simple testing. Usually, the temperature to which the substrate is heated is above about 80° C. The substrate may be heated in a conventional manner, for example, by resistance heating, inductive heating, or electric heating, or the substrates may be heated by radiation energy. Laser energy is particularly suitable for this. Laser heating is particularly advantageous in that lasers can be focused, and therefore can specifically heat limited areas on the substrate.

An apparatus for thermal chemical vapor deposition is typically pressure tight such as are used in high vacuum techniques as this process is typically carried out under reduced pressure. The apparatus may comprise gas lines which can be heated for carrying the metal complexes or the inner gas, blockable gas inlets and outlets, temperature measuring means if decomposition is to be induced by radiation, a radiation source must also be present. In operation, the metal complex is introduced into the apparatus in the vapor phase. An inert or reactive carrier gas may be included.

Decomposition of the metal complex may be brought about as discussed above. For example, the decomposition may be plasma induced by a D.C. plasma, high-frequency plasma, microwave plasma or glow discharge plasma. Alternately photolytic decomposition may be effected by using a laser operating at a suitable wavelength.

The thickness of the layer deposited typically depends on the length of the deposition, on the partial pressure in the gas phase, on the flow rate of the gas and on the decomposition temperature. Depending on the desired layer thickness, a person skilled in the art can readily determine the time and deposition temperature required to produce a layer of a given thickness by simple tests.

If the metal complex is decomposed under an atmosphere of an inert gas, for example, argon, metal-containing layers are typically deposited in which the metal is essentially metallic form. The decomposition may also be carried out under a reactive gas atmosphere, including a reducing atmosphere, an oxidizing atmosphere, and a hydrolyzing or carbonizing atmosphere. A reducing atmosphere with hydrogen as the reactive gas is typically used for deposition of layers containing metals, for example, copper. Where the decomposition is carried out under an oxidizing atmosphere, for example, one containing oxygen, nitrogen dioxide or ozone, layers containing the metal in the form of an oxide are formed. Alternatively, it is also possible to operate in a hydrolyzing or carbonizing atmosphere, for instance, in the presence of water and/or carbon dioxide. The metal carbonate or hydroxide which is produced as an intermediate stage may be subsequently calcined to form the metal oxide. In addition, use of ammonia as a reactive gas yields layers containing the metal in the form of a nitride.

The process according to the invention is also suitable for depositing layers which contain one or more metals. In this case, the deposition process is characterized in that for depositing layers containing more than one metal, one or more compounds of formula II or other formulas are decomposed simultaneously or successively.

EXAMPLES Example 1

Preparation of (CH₃)₃CCOCH₂COSi(CH₃)₃(IV) via Claisen Condensation of a Lithium Enolate and an Acid Chloride

A two liter 3-neck flask held at 0°-C. was equipped with a magnetic stirrer, a rubber septum and a silicon oil bubbler under a positive flow of nitrogen gas. The flask was charged with anhydrous diethyl ether (250 mL) and diisopropylamine, (11.3 mL, 86.2 mmol), 2.5 M solution of n-BuLi in hexane (34.5 mL, 86.2 mmol) was added very slowly to the stirred solution. Once addition of the n-BuLi was complete the reaction temperature was maintained at 0° C. for 1 h to ensure generation of lithium diisopropylamide, (LDA). The temperature was lowered to −85° C. and acetyltrimethylsilane (10.0 g, 86.2 mmol), was then added slowly to the mixture. A smooth exothermic reaction ensued which resulted in the formation of corresponding organolithium anion, (Me₃Si(C)(OLi)CH₂). A second one-liter single-neck flask held at −110° C. equipped with a magnetic stirrer, a rubber septum and under a positive flow of nitrogen gas, was charged with anhydrous diethyl ether (250 mL) and trimethylacetylchloride, (10.6 mL, 86.2 mmol). After 10 minutes the labile trimethylsilylorganolithium anion, (Me₃Si(C)(OLi)CH₂), was slowly transferred to the second flask via a cannula the reaction temperature was maintained between −110° C. and −75° C. After 1 hour, the reaction was essentially complete and was quenched with saturated ammonium chloride solution. Purification of the silyl β-diketonate was effected via flash column chromatography using a 100:1 (hexane: diethyl ether) eluant.

Example 2

Preparation of IV via Claisen Condensation of a Lithium Enolate and an Ester

A two liter 3-neck flask held at 0° C. equipped with a magnetic stirrer, a rubber septum and a silicon oil bubbler and under a positive flow of nitrogen gas was charged with anhydrous diethyl ether (250 mL) and diisopropylamine, (11.3 mL, 86.2 mmol). n-Butyllithium (34.4 mL, 86.2 mmol, 2.5 M in hexane) was added very slowly to the stirred solution. Once addition of the n-BuLi was complete, the reaction temperature was maintained at 0° C. for 1 hour to ensure generation of lithium diisopropylamide, (LDA). The temperature was then lowered to −85° C. and acetyltrimethylsilane (10.0 g, 86.2 mmol) was added slowly to the mixture. A smooth exothermic reaction ensued which resulted in the formation of corresponding lithium enolate, (Me₃Si(C)(OLi)CH₂). A second one-liter single-neck flask held at −110° C. equipped with a magnetic stirrer, a rubber septum and under a positive flow of nitrogen gas, was charged with anhydrous diethyl ether (250 mL) and methyl pivaloate, (10.6 mL, 86.2 mmol). After 10 minutes, the reactive lithium enolate, (Me₃Si(C)(OLi)CH₂), was slowly transferred to this mixture via a cannula while the reaction temperature was maintained between −110° C. and −75° C. After 2 hours, the reaction was essentially complete and was then quenched with saturated ammonium chloride solution. Purification of the silyl β-diketonate was effected via flash column chromatography using a 100:1 (hexane: diethyl ether) solvent system.

Example 3

Preparation of IV via Pseudo Barbier Conditions

Trimethylsilyllithium, (18 mmol) was prepared according to the literature method (Still, W. C., J. Org. Chem., 41, 3063-3064 (1976)) and then transferred via cannula to a second reaction flask held at −78° C., charged with anhydrous diethyl ether, (150 mL) and methyl 4,4-dimethyl-3-oxopentanoate, (CH₃)₃CCOCH₂CO₂CH₃ (2.09 g, 18 mmol), which resulted in the dissipation of the red colour. (Gasking, E. I.; Whitman, G. H. J. Chem. Soc., Perkin Trans. 1, 1985, 409-414) After 30 minutes the reaction was quenched with saturated ammonium chloride, (100 mL) and copper acetate(II) monohydrate, (3.60 g, 18 mmol) was added to yield the crude silyl β-diketonate copper complex. Subsequent purification yielded pure metal complex.

Example 4

Preparation of IV by the Dithiane Route

A 3-neck flask held at −30° C. was equipped with a magnetic stirrer, a rubber septum and a silicon oil bubbler was under a positive flow of nitrogen gas. The flask was charged with anhydrous THF (30 mL) and 2-trimethylsilane-1,3-dithiane, (3.8 mL, (20 mmol). n-Butyllithium (8.0 mL, 20 mmol, 2.5 M in hexane) was added very slowly to the stirred solution. Once addition of n-BuLi was complete the reaction temperature was maintained at −30° C. for 24 hour to ensure generation of 2-lithio-1,3 dithiane. The anion was transferred via a cannula to a second flask maintained at −60° C. and charged with an ethereal solution of CuBr.Me₂S (2.06 g, 10 mmol). After approximately one hour the formation of the 2-lithio-1,3-dithianylcuprate was essentially complete. Bromo pinacolone, (CH₃)₃CCOCH₂Br, dissolved in ether, was then added slowly to the organocuprate and was allowed to react for 24 hour at −30° C. The reaction was quenched with saturated ammonium chloride solution. Vacuum distillation (125-130° C., 0.5 mm Hg) afforded the pure product.

Deprotection of the dithiane protected silyl β-diketonate was achieved by treatment with mercuric oxide and mercuric chloride in an aqueous alcoholic solution for 1.5 hours, yielding the desired the silyl β-diketonate upon filtration and concentration.

Example 5

Formation of Co((CH₃)₃CCOCHCOSi(CH₃)₃)₃ Under Protic Conditions

A solution of IV (0.54 g, 2.7 mmol) prepared as in Example 1 in aqueous ethanol (80 mL) was prepared. To the stirred solution, an aqueous ethanolic solution of sodium hydroxide (0.1 g, 3 mmol) was slowly added and allowed to react approximately 15 minutes. The slow addition of this solution to cobalt (II) chloride hexahydrate, (0.30 g, 1.4 mmol) dissolved in aqueous ethanol resulted in the formation of a deep green solution. The solvent was removed in vacuo to leave behind the crude cobalt (III) silyl β-diketonate complex. Addition of pentane and water, followed by subsequent work-up and sublimation resulted in isolation of the analytically pure metal complex.

Example 6

Formation of Cu((CH₃)₃CCOCHCOSi(CH₃)₃)₂ Under Aprotic Conditions

Under aprotic conditions, IV (0.25 g 1.3 mmol), prepared as in Example 1, was dissolved in THF (100 mL). To the stirred solution, potassium hydride, (KH), (0.05 g, 1 mmol) was added slowly and allowed to react for approximately 30 minutes. The addition of copper (II) chloride dihydrate, (0.11 g, 6.3 mmol) portionwise resulted in the formation of a deep green solution. The reaction was then quenched carefully with water and extracted with pentane. The solvent was then removed in vacuo to leave behind the copper (II) silyl β-diketonate complex, which on sublimation yielded the analytically pure metal complex.

Example 7

Formation of Cu((CH₃)₃CCOCHCOSi(CH₃)₃)₂ Under Protic Conditions

Under protic conditions, IV (0.25 g, 1.3 mmol), prepared as in Example 1, was dissolved in aqueous ethanol (80 mL). To the stirred solution, an aqueous ethanolic solution of sodium hydroxide (0.1 g, 3 mmol) was slowly added and allowed to react approximately 15 minutes. Copper (II) chloride dihydrate, (0.11 g, 6.3 mmol) was then added which resulted in the formation of a deep green solution. The solvent was then removed in vacuo to leave behind the copper (II) silyl β-diketonate complex. Sublimation resulted in the isolation of analytically pure metal complex.

Example 8

Direct Formation of Cu((CH₃)₃CCOCHCOSi(CH₃)₃)₂ Using Crude IV

To a stirred solution of crude IV (2.73 g, 13.8 mmol) dissolved in THF (100 mL), a slurry of excess copper (II) acetate hydrate, (5.46 g, 27.4 mmol) in aqueous THF was added. Upon addition, a deep green solution formed. Extraction, washing, drying, and concentration resulted in isolation of a green oil. Column chromatography on silica gel using a 100:1 hexane-ether eluant system yielded semi-pure silyl β-diketonate copper (II) complex. Controlled sublimation resulted in the formation of analytically pure metal complex.

Example 9

Direct Formation of Cu((Ch₃)₃CCOCHCOSi(Ch₃)₃)₂ Using Pure IV

To a stirred solution of pure IV, (5.00 g, 25 mmol) dissolved in THF (100 mL), a slurry of copper (II) acetate hydrate, (3.00 g, 15 mmol) in aqueous THF was added. Upon addition, a deep green solution formed. Extraction, washing, drying, and concentration in vacuo resulted in isolation of the copper(II) silyl β-diketonate complex. Sublimation resulted in the formation of analytically pure metal complex.

Example 10

Preparation of Cu(I)((Ch₃)₃CCOCHCOSi(Ch₃)₃).COD

Under anaerobic conditions, 1,5-cyclooctadiene (0.1 g, 1 mmol) was added dropwise to a suspension of copper (I) chloride in THF. The suspension was stirred for 10 minutes, after which a solution of the potassium salt of IV (prepared by the addition of potassium hydride (0.05 g, 1 mmol) over 30 minutes to a solution of IV (0.25 g, 1.3 mmol)), was carefully added via syringe and allowed to react for approximately 3 hours. The resultant copper(I) silyl β-diketonate complex was isolated by subsequent anhydrous work-up.

Example 11

Formation of Mn((Ch₃)₃CCOCHCOSi(CH₃)₃)₃ via Lewis Base

A solution of IV (0.54 g, 2.7 mmol) in aqueous ethanol (80 mL) was prepared. To the stirred solution was slowly added an aqueous ethanolic solution of sodium hydroxide (0.1 g, 3 mmol). The resultant solution was stirred for approximately 15 minutes and then slowly added to manganese (II) chloride (0.176 g, 1.4 mmol) dissolved in aqueous ethanol which resulted in the formation of a dark green solution. The solvent was removed in vacuo to leave behind the crude manganese(III) silyl β-diketonate complex. Addition of pentane and water followed by subsequent work-up and sublimation yielded an analytically pure metal complex.

Example 12

Preparation of Cu((Ch₃)₃CCSCHCOSi(Ch₃)₃)₂ via Claisen Condensation of Lithium Enolate and Thioacid Chloride

A two liter 3-neck flask held at 0° C. was equipped with a magnetic stirrer, a rubber septum and a silicon oil bubbler under a positive flow of nitrogen gas. The flask was charged with anhydrous diethyl ether (250 mL) and diisopropylamine (11.3 mL, 86.2 mmol). n-Butyllithium (34.5 mL of a 2.5 M solution in hexane, 86.2 mmol) was added very slowly to the stirred solution. Once the addition of BuLi was complete, the reaction temperature was held at 0° C. for 1 hour to ensure generation of lithium diisopropylamide, (LDA). The temperature was lowered to −85° C. and acetyltrimethylsilane (10.0 g, 86.2 mmol) was added slowly to the mixture. A smooth exothermic reaction ensued which resulted in the formation of corresponding organolithium enolate, (Me₃Si(C)(OLi)CH₂). A second one liter single-neck flask held at −110° C. and equipped with a magnetic stirrer, a rubber septum under a positive flow of nitrogen gas, was charged with anhydrous diethyl ether (250 mL) and trimethylthioacetylchloride, (10.6 mL, 86.2 mmol). After 10 minutes, the labile trimethylsilylorganolithium anion, (Me₃Si(C)(OLi)CH₂), was slowly transferred to the second flask via cannula while maintaining the reaction temperature between −110° C. and −75° C. After 1 hour the reaction was quenched with saturated ammonium chloride solution. Purification of the silyl β-thioketonate can be effected by flash column chromatography using a 100:1 (hexane: diethyl ether) eluant. The proton NMR spectrum of the product gave the expected results.

Example 13

Volatility of Metal Complexes with Silyl β-Diketonates and Silyl β-Thioketonates

Thermogravimetric analysis (TGA) was performed on samples of the metal complexes listed in Table 3. The samples were heated at a rate of 10° C./min under an argon atmosphere. Weight loss was associated with transformation of the complexes into the vapor phase. The TGA curves showed rapid and complete volatilization of the complexes over a narrow temperature range, indicating the absence of decomposition under the conditions employed. The inflection point of the curve is taken as the temperature at which approximately 50% of the sample by weight has volatilized. This temperature, listed as T_(50%) in the table, is a measure of relative volatility, and is tabulated for each compound. The T_(50%) values range from a low of about 111° C. for the fluorinated compound Cu(CF₃COCHCOSi(Ch₃)₃)₂, to a high of about 170° C. for a complex with a phenyl-substituted ligand, Cu(C₆H₅COCHCOSi(Ch₃)₃)₂. The last entry in the table, for Cu(H₂C=(Ch₃)COCHCOSi(Ch₃)₃)₂, showed a two-stage volatilization.

TABLE 3 Volatility of Metal Diketonate Complexes Metal Complex T_(50%), ° C. CU((CH₃)₃CCOCHCOSi(CH₃)₃)₂ 158 CO((CH₃)₃CCOCHCOSi(CH₃)₃)₃ 167 Mn((CH₃)₃CCOCHCOSi(CH₃)₃)₃ 119 Cu((CH₃COCHCOSi(CH₃)₃)₂ 155 CU(CH₃CH₂COCHCOSi(CH₃)₃)₂ 150 CU(CH₃CH₂CH₂COCHCOSi(CH₃)₃)₂ 152 CU(CH₃(CH₂)₃COCHCOSi(CH₃)₃)₂ 158 CU((CH₃)₂CHCOCHCOSi(CH₃)₃)₂ 137 CU((CH₃)₂CHCH₂COCHCOSi(CH₃)₃)₂ 161 CU(CF₃COCHCOSi(CH₃)₃)₂ 111 Cu(CF₃(CF₂)₂COCHCOSi(CH₃)₃)₂ 120 Cu(C₆H₅COCHCOSi(CH₃)₃)₂ 170 Cu(H₂C═(CH₃)COCHCOSi(CH₃)₃)₂ 134, 234

Example 14

Chemical Vapor Deposition of Copper

Copper films were deposited on fragments of silicon wafers, including wafers having surfaces composed of silicon, silicon dioxide, patterned silicon dioxide, and tungsten nitride, using a copper (II) silyl β-diketonate precursor of composition Cu((Ch₃)₃CCOCHCOSi(Ch₃)₃)₂.

A cold wall stainless steel single wafer CVD reactor was employed for the depositions. The wafers were loaded into the chamber through a door and placed on a resistively heated stainless steel pedestal bearing a quartz plate and heated to 300° C. under a flowing hydrogen ambient atmosphere. The actual temperature of the wafer was measured via a thermocouple contacting the top side of the wafer. The system pressure was then reduced to the desired deposition pressure of 500 mTorr. The pressure was maintained throughout the time of the deposition using an automated throttle valve.

A source of the precursor was maintained at 140° C. The precursor was delivered to the reactor by means of a hydrogen carrier/reactant gas bubbler at a flow rate of 60 sccm at approximately 500 mTorr. After the deposition, the carrier gas flow was terminated, the source was closed to the reactor, and the chamber was evacuated to less than 20 mTorr and then flushed with nitrogen gas. The heater was allowed to cool under a flow of nitrogen. The test wafers were retrieved from the reactor through the door of the reactor.

The resulting copper films were smooth and exhibited high conformality at thicknesses ranging from 100 Å to 3000 Å (10 nm to 300 nm).

Example 15 Preparation of Cu(II) Complex with 2,2,6,6-Tetramethyl-2-Germa-3,5-heptanedione (Cu(tmghd)₂)

Preparation of Acetyltrimethylgermane

The addition of one equivalent of tert-butyllithium to a THF solution of distilled ethyl vinyl ether at −110° C. resulted in a highly exothermic reaction, the internal temperature rose to −78° C. with concomitant formation of a yellow precipitate. On completion of the addition, the yellow solid dissolved when the temperature of the reaction was maintained at −25° C. After 30 minutes, metallation was essentially complete with no evidence of decomposition of the lithium reagent. The solution was then cooled to −85° C. and chlorotrimethylgermane was added slowly so that the reaction temperature did not exceed −80° C. After allowing the reaction to warm to room temperature over 4 h, the crude germylated product was isolated by quenching with saturated NaHCO₃ solution, extracted with pentane, dried over Na₂SO₄ and concentrated in vacuo. ¹H and ¹³C NMR of the clear solution was consistent with the formation of H₂C=C(OEt)GeMe₃. ¹H NMR (CDCl₃): δ4.49 (d, J=1.78 Hz 1H,=CH₂),4.41 (d,J=1.78 Hz 1H,=CH₂),3.68 (q,2H, —CH₂),1.26 (t, 3H, CH₂—CH₃),0.23 (s, 9H, Ge—CH₃). ¹³C NMR (CDCl₃): δ171.84 (C—OEt), 91.38 (=CH₂), 62.20 (O—CH₂CH₃) 14.49 (CH₃—CO), −2.48 (Ge—CH₃); yield =77.6%.

The α-germa-vinyl ether was then hydrolyzed to acetyltrimethylgermane with acid. The yield of the hydrolysis was dependent on the scale of hydrolysis. On a 0.010 mol scale, acidic hydrolysis (3N HCl/Et₂O) gave the acetyl derivative in greater than 90% yields. However, on larger scale (0.14 mol), even with vigorous mechanical stirring, at best only 82% conversion was possible. The hydrolysis was monitored via TLC (10:1, hexane/ethyl acetate) to ascertain complete conversion to the ketone. After work-up and short path flash distillation at 62° C. and 40 mmHg, multinuclear NMR spectroscopy confirmed the product as acetyltrimethylgermane. ¹H NMR (CDCl₃):δ2.32 (s, 3H, —CH₃), 0.35 (s, 9H,(Ge(Ch₃)₃). ¹³C NMR (CDCl₃): δ244.92 C═O), 36.37 (Ch₃—CO),−3.10 (Ge—CH₃); Anal. Calcd for C₅H₁₂OGe: C, 37.36; H, 7.52. Found: C, 37.47; H, 7.76.

Preparation of 2,2,6,6-Tetramethyl-2-germa-3,5-heptanedione (tmghdH)

The germa-β-diketone, tmghH, was prepared by the reaction of acetyltrimethyl-germane (10 mmol) with freshly prepared LDA (10 mmol) in dry diethyl ether (50 mL) to generate the lithium enolate. After 30 minutes the enolate was slowly transferred to the second flask charged with anhydrous diethyl ether (50 mL) and trimethylacetylchloride, (10 mmol) and the reaction temperature was maintained between −110° C. and −85° C. After 1 hour, the reaction was essentially complete and was quenched with saturated ammonium chloride solution. Purification of the germa-β-diketone via flash column chromatography using hexane as eluant afforded the product. (61% yield) ¹H and ¹³C NMR spectroscopy showed the diketone to exist as the enolic tautomer. ¹H NMR (CDCl₃): δ15.17 (s, 1H, OH), 5.84 (s, 1H,═CH), 1.14 (s, 9H, ^(t)Bu—CH₃),−0.33 (s, 9H, Ge—CH₃). ¹³C NMR (CDCl₃): δ207.80 (C═O), 199.17 (C—OH), 103.60 (═CH), 41.27 (C(Ch₃)₃), 27.02 (^(t)Bu—CH₃), −3.10 (Ge—CH₃); Anal. Calcd for C₁₀H₂₀O₂Ge: C, 49.05; H, 8.23. Found: C, 50.71; H, 8.49.

The copper(II) complex, Cu(tmghd)₂, was prepared by the method used above and was purified via sublimation (99° C., 0.1 mm Hg) (48% yield). Anal. Calcd for C₂₀H₃₈CuO₄Ge₂: C, 43.57; H, 6.95. Found: C, 43.80; H, 7.48. M.p.: 148° C.

Crystals of Cu(tmghd)₂ suitable for single crystal X-ray diffraction studies were obtained by controlled growth from pentane at 5° C. over 7 days. The complex was square planar with the copper atom located on a center of symmetry. Disorder associated with occupancy of the t-butyl and trimethylgermyl sites limited the accuracy of the structure determination. Modifying crystal growth parameters, such as solvent system, temperature, or even growth by slow sublimation, all yielded crystals with the same unit cell. Incorporation of the germanium atom into the βdiketonate architecture imposed modest structural differences when compared with a copper complex with the sila-β-diketonate 2,2,6,6-tetramethyl-2-sila-3,5-heptanedione (Cu(tmshd)₂), consistent with the larger van der Waals radius of germanium.

Thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC) facilitated evaluation of the volatility and thermal stability of the copper complex. Following drying in vacuo,(60° C., 0.5 mm Hg) the complexes were analyzed in a dynamic dinitrogen atmosphere at ambient pressure. The sublimation of Cu(tmghd)₂ has an onset of 89° C., with less then 1% residue. Calculation of the derivative weight loss, (%/°C.), reveals the maximum rate of weight loss to occur at 155° C. Although Cu(tmghd)₂ has a molecular weight 28% greater than Cu(tmhd)_(2,) it is more volatile. DSC analysis of a hermetically sealed sample of had a phase change attributed to melting at 148° C., with complete decomposition occurring after 200° C. is reached. Although Cu(tmghd)₂ displays apparently lower volatility than Cu(tmshd)_(2,) Cu(tmghd)₂ has a much higher decomposition temperature.

Example 16

TGA and DSC Analysis of Copper Complexes α-Germa-β-Diketones

The thermal properties of copper complexes of other germyl ligands were prepared by the process illustrated in Example 15 were evaluated. Results appear in Table 4.

TABLE 4 Copper Complexes With Germyl Ligands TGA DSC Analysis Weight Decomp. T, R¹ E¹R³R⁴R⁵ T₅₀, ° C. Loss, % M_(p), ° C. ° C. Me GeMe₃ 165 97.4 153 204 Et GeMe₃ 162 94.6 100 198 n-Pr GeMe₃ 161 95.1 65 194 i-Pr GeMe₃ 155 96 71 206 i-Bu GeMe₃ 171 94.1 96 200 t-Bu GeMe₃ 159 97.7 148 199 (CF₃)₂Me GeMe₃ 147 100 146 180 C(F₆-t-Bu) CF₃ GeMe₃ 127 98.6 92 200 C₂F₅ GeMe₃ 114 99.3 64 159 n-C₃F₇ GeMe₃ 128 99 — —

Example 17 Preparation of Copper (II) Complex With (6,6-dimethyl-9,9,10,10,11,11,12, 12,13,13,14,14,15,15,16,16,16-heptadecafluoro-6-silahexadeca-3,5-dionate)(Cu[C₂F₅—SiMe₂C₁₀H₄F₁₇]₂)

Acetyldimethyl-3,3,4,4,5,5,6,6,7,7,8,8,9,9,10,10,10-heptadecafluorodecylsilane was synthesized from ethyl vinyl ether and chlorodimethyl-3,3,4,4,5,5,6,6,7,7,8,8,9,9,10,10-heptadecafluorodecylsilane after the procedure of Cunico and Kuan (J. Org. Chem. 1985, 50, 5410-5413).

Preparation of 6,6-dimethyl-9,9,10,10,11,11,12,12,13,13,14,14,15,15,16,16,16-heptadecafluoro-6-silahexadeca-3,5-dione (C₂F₅—SiMe₂C₁₀H₄F₁₇)

A stirring solution of diisopropylamine (0.51 mL, 3.6 mmol) and Et₂O (70 mL) in a 250 mL Schlenk flask was cooled to 0° C. n-BuLi (1.4 mL, 3.6 mmol, 2.5 M in hexanes) was added and the solution stirred for 1 h and then cooled to −50° C. A solution of acetyldimethyl-3,3,4,4,5,5,6,6,7,7,8,8,9,9,10,10,10-heptadecafluorodecylsilane (2.0 g, 3.6 mmol) dissolved in Et₂O (10 mL) was added slowly. After 1 h, the mixture of the enolate was cannulated to another 250 mL Schienk flask containing a solution of methyl pentafluoropropionate (0.47 mL, 3.7 mmol) in Et₂O (40 mL) at −50° C. The mixture was stirred for 3 h at −50° C. and then quenched with aqueous saturated NH₄Cl solution. The organic layer layer was separated, washed with water and dried with Na₂SO4. Filtration followed by evaporation of the solvent in vacuo gave the crude product as a light yellow oil. Yield: 2.2 g, 87%. ¹H NMR (CDCl₃): δ6.12 (s, 1H), 2.2-2.0 (m, 2H), 1.0-0.9 (m, 2H), 0.30 (s, 6H). ¹⁹F: δ−81.66 (t, 3F, J=10.0 Hz),−83.71 (s, 3F),−116.77 (m, 2F),−122.64 (br, 6F),−123.46 (br, 2F),−123.98 (br, 2F),−124.9 (s, 2F),−126.90 (br, 2F).

Preparation of Copper(II) bis(6,6-dimethyl-9,9,10,10,11,11,12,12,13,13,14,14,15,15, 16,16,16-heptadecafluoro-6-silahexadeca-3,5-dionate) (Cu[C₂F₅—SiMe₂C₁₀H₄F₁₇]₂)

The copper (II) complex with the heptadecafluorodecylsilane ligand above was prepared and isolated according to the procedure in Example 9. Single crystals suitable for X-ray diffraction studies were grown from CH₂Cl₂/ Hexane at room temperature. Anal. Calcd (found) for C₃₄H₂₂O₄F₄₄Si₂Cu: C, 28.16 (28.37); H, 1.53 (1.76).

Examples 18-21

TGA and DSC Analysis of Copper Complexes

Volatility of copper (II) complexes with alkyl-substituted and fluoroalkyl-substituted silyl ligands was determined by thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC). Following drying in vacuo,(60° C., 0.5 mm Hg) the complexes were analyzed in a dynamic nitrogen atmosphere at ambient pressure. Conditions for the DSC analyses were: ramp rate at 1° C./min in dry N₂ stream (100 cm³/min). Measurement conditions for TGA were: ramp rate at 10° C./min in dry N₂ stream (40 cm³/min). Derivative weight loss, (%/° C.), the maximum rate of weight loss was calculated and is listed in the following Tables as T_(50%).

Example 18

Copper (II) Complexes with Non-fluorinated Ligands

Thermal properties of copper (II) complexes with non-fluorinated ligands were determined as described above. Results appear in Table 5.

TABLE 5 Copper Complexes With Non-Fluorinated Ligands TGA DSC Analysis T₅₀, Weight Decomp. R¹ E¹R³R⁴R⁵ ° C. Loss, % M_(p), ° C. T, ° C. Me SiMe₃ 155 96.3 93 189 Et SiMe₃ 147 95.2 96 171 n-Pr SiMe₃ 160 91.5 68 172 i-Pr SiMe₃ 148 96.0 94 159 n-Bu SiMe₃ 161 91.0 43 174 i-Bu SiMe₃ 152 92.4 102 166 s-Bu SiMe₃ 149 96.1 107 167 t-Bu SiMe₃ 163 98.2 161 176 Me SiEt₃ 185 93.8 47 208 Et SiEt₃ 183 95.9 — 203 n-Pr SiEt₃ 192 95.4 — 199 i-Pr SiEt₃ 190 92.5 — — n-Bu SiEt₃ 197 90.6 — 199 i-Bu SiEt₃ 192 93.4 — 200 s-Bu SiEt₃ 188 95.6 — 195 t-Bu SiEt₃ 192 95.3 — — Me Si(t-Bu)Me₂ 174 97.8 — — Et Si(t-Bu)Me₂ 176 97.2 86 208 n-Pr Si(t-Bu)Me₂ 184 97.5 80 215 i-Pr Si(t-Bu)Me₂ 174 99.0 — — n-Bu Si(t-Bu)Me₂ 197 98.1 41 214 i-Bu Si(t-Bu)Me₂ 188 98.9 87 209 s-Bu Si(t-Bu)Me₂ 182 99.2 99 219 t-Bu Si(t-Bu)Me₂ 182 95.9 — — Me SiMe₂C(Me)₂CHMe₂ 202 95.1 76 227 Et SiMe₂C(Me)₂CHMe₂ 203 91.9 89 224 n-Pr SiMe₂C(Me)₂CHMe₂ 213 94.9 50 234 i-Pr SiMe₂C(Me)₂CHMe₂ 209 98.1 — — n-Bu SiMe₂C(Me)₂CHMe₂ 218 93.6 — 229 s-Bu SiMe₂C(Me)₂CHMe₂ 209 95.7 56 236 t-Bu SiMe₂C(Me)₂CHMe₂ 207 95.9 101 228 Et Si(i-Pr)₃ 218 96.8 — — i-Pr Si(i-Pr)₃ 223 96.7 — — i-Bu Si(i-Pr)₃ 218 92.3 — 237 s-Bu Si(i-Pr)₃ 215 96.0 75 238 t-Bu Si(i-Pr)₃ 217 98.4 68 245

Example 20

Copper (II) Complexes with Ligands Containing Short-Chain Fluoroalkyl Group

Thermal properties of copper (II) complexes with ligands containing short-chain fluoroalkyl groups were determined as described above. Results appear in Table 6.

TABLE 6 Copper Complexes with Ligands Containing Short-Chain Fluoroalkyl Groups TGA DSC Analysis T₅₀, Weight Decomp. R¹ E¹R³R⁴R⁵ ° C. Loss, % M_(p), ° C. T., ° C. (CF₃)₂MeC SiMe₃ 144 99.8 143 189 CF₃ SiMe₃ 112 97.5 93 186 C₂F₅ SiMe₃ 113 99.4 75 183 n-C₃F₇ SiMe₃ 119 95.8 38 192 i-C₃F₇ SiMe₃ (CF₃)₂MeC SiEt₃ 170 99.2 57 207 CF₃ SiEt₃ 154 97.8 82 220 C₂F₅ SiEt₃ 150 99.9 217 n-C₃F₇ SiEt₃ 154 89.7 227 i-C₃F₇ SiEt₃ (CF₃)₂MeC Si(t-Bu)Me₂ 176 99.5 163 242 CF₃ Si(t-Bu)Me₂ 153 98.5 C₂F₅ Si(t-Bu)Me₂ 152 99.6 73 ??? n-C₃F₇ Si(t-Bu)Me₂ 169 99.2 56 242 i-C₃F₇ Si(t-Bu)Me₂ 157 98.4 157 242 (CF₃)₂MeC SiMe₂ 184 99.8 130 238 C(Me)₂CHMe₂ CF₃ SiMe₂ 174 98.6 C(Me)₂CHMe₂ C₂F₅ SiMe₂ 172 99.3 79 249 C(Me)₂CHMe₂ n-C₃F₇ SiMe₂ Await- C(Me)₂CHMe₂ ing i-C₃F₇ SiMe₂ 165 98.5 122 252 C(Me)₂CHMe₂ (CF₃)₂MeC Si(i-Pr)₃ 189 96.8 CF₃ Si(i-Pr)₃ 181 95.11 C₂F₅ Si(i-Pr)₃ 182 99.2 72 252 n-C₃F₇ Si(i-Pr)₃ 185 98.0 — 255 i-C₃F₇ Si(i-Pr)₃

Example 21

Copper (II) Complexes with Ligands Containing Long-Chain Fluoroalkyl Group

Thermal properties of copper (II) complexes with ligands containing long-Chain fluoroalkyl groups were determined as described above. Results appear in Table 7.

TABLE 7 Copper Complexes with Ligands Containing Long-Chain Fluoroalkyl Group TGA DSC Analysis T₅₀, Weight M_(p), Decomp. R¹ E¹R³R⁴R⁵ ° C. Loss, % ° C. T., ° C. Me SiMe₂(CH₂)₂(CF₂)₇CF₃ 181 94.1 129 179 i-Pr SiMe₂(CH₂)₂(CF₂)₇CF₃ 156 98.4 59 167 t-Bu SiMe₂(CH₂)₂(CF₂)₇CF₃ 159 94.2 113 158 dec CF₃ SiMe₂(CH₂)₂(CF₂)₇CF₃ 196 98.0 63 198 C₂F₅ SiMe₂(CH₂)₂(CF₂)₇CF₃ 196 98.6 66 203 n-C₃F₇ SiMe₂(CH₂)₂(CF₇CF₃ 189 99.8 61 215 CH₃ SiMe₂(CH₂)₂(CF₂)₅CF₃ 174 91 106 186 i-Pr SiMe₂(CH₂)₂(CF₂)₅CF₃ 171 96 81 172 n-Bu SiMe₂(CH₂)₂(CF₂)₅CF₃ 181 96 78 172 t-Bu SiMe₂(CH₂)₂(CF₂)₅CF₃ 161 96 92 177 CF₃ SiMe₂(CH₂)₂(CF₂)₅CF₃ 168 96 47 194 C₂F₅ SiMe₂(CH₂)₂(CF₂)₅CF₃ 165 98 31 194 C₃F₇ SiMe₂(CH₂)₂(CF₂)₅CF₃ 169 98 45 189

Example 22

Formation of Pd((Ch₃)₃CCOCHCOSi(Ch₃)₃)₂

Palladium dichloride (0.12 g) was added to the sodium salt of IV in about 100 ml distilled THF. After about 13 hours, color of the solution changed from red to reddish green. The crude product was recovered and sublimed for purification, yielding an off-yellow product, 28% yield.

TGA: T_(50%) 142° C., 99.1% weight loss.

DSC: Melting point 147° C.; decomposition 347° C.

Elemental analysis: Calculated: C,47.56; H,7.58; Found: C,47.53; H,7.68, 

What is claimed:
 1. A compound of formula I:

wherein R¹ is methyl, ethyl, isopropyl, n-propyl, isobutyl, s-butyl, n-butyl, CF₃, C₂F_(5,) i-C₃F₇, n-C₃F₇, or —C(CH₃)(CF₃)₂; R² is H; E¹ is Si or Ge; R³, R⁴, and R⁵ are independently C₆ or lower alkyl; and Y and Z are O.
 2. A compound according to claim 1, wherein E¹ is Ge.
 3. A compound according to claim 2, wherein R¹ is methyl.
 4. A compound according to claim 2, wherein R¹ is ethyl.
 5. A compound according to claim 2, wherein R¹ is isopropyl.
 6. A compound according to claim 2, wherein R¹ is n-propyl.
 7. A compound according to claim 2, wherein R¹ is isobutyl.
 8. A compound according to claim 2, wherein R¹ is s-butyl.
 9. A compound according to claim 2, wherein R¹ is s-butyl.
 10. A compound according to claim 2, wherein R¹ is n-butyl.
 11. A compound according to claim 2, wherein R¹ is CF₃.
 12. A compound according to claim 2, wherein R¹ is C₂F₅.
 13. A compound according to claim 2, wherein R¹ is i-C₃F₇.
 14. A compound according to claim 2, wherein R¹ is n-C₃F₇.
 15. A compound according to claim 2, wherein R¹ is C(CH₃)(CF₃)₂.
 16. A compound according to claim 1, wherein E¹ is Si.
 17. A compound according to claim 16, wherein R³, R⁴, and R⁵ are methyl.
 18. A compound according to claim 16, wherein R³, R⁴, and R⁵ are ethyl.
 19. A compound according to claim 16, wherein R³, R⁴, and R⁵ are t-butyl.
 20. A compound according to claim 16, wherein R³, R⁴, and R⁵ are isopropyl.
 21. A compound according to claim 16, wherein R³ and R⁴ are methyl, and R⁵ is C(CH₃)₂CH(CH₃)₂.
 22. A metal-ligand complex of formula II: M L_(n)·pD  (II) wherein M is a metal chosen from the group consisting of: Li, Na, K, Rb, Cs, Mg, Ca, Sr, Ba, Sc, Y, La, Ce, Ti, Zr, Hf, Pr, V, Nb, Ta, Nd, Cr, Mo, W, Mn, Re, Sm, Fe, Ru, Eu, Os, Co, Rh, Ir, Gd, Ni, Pd, Pt, Tb, Cu, Ag, Au, Dy, Ho, Al, Ga, In, Tl, Er, Ge, Sn, Pb, Tm, Sb, Bi, Yb, Lu, Th, and U, and mixtures thereof; D is a neutral coordinating ligand; n is equal to the valence of M; p is zero or an integer from 1 to 6; and L is a ligand of formula III:

 wherein R¹ is methyl, ethyl, isopropyl, n-propyl, isobutyl, s-butyl, n-butyl, CF₃, C₂F₅, i-C₃F₇, n-C₃F₇, or —C(CH₃)(CF₃)₂; R² is H; E¹ is Si or Ge; R³, R⁴, and R⁵ are independently C₆ or lower alkyl; and Y and Z are O. 